DIN abrasion tester TDAT-A10 determines abrasion resistance of rubber made products, natural rubber, vulcanized rubber, thermoplastic amorphous polymers to withstand the long term damage as a result of friction due to its excessive use. The ratio between standard loss of rubber material & test rubber material, expressed in percentage, marks the abrasion resistance index of sample under test.
| Test arm weight | 2.5 N |
| Additional Loads | 2.5 ± 0.1 N, 5 ± 0.1 N, 10 ± 0.1 N, |
| Idler | 150 mm |
| Abrasion stroke | 40 ± 0.2 M |
| Horizontal displacement | 4.2 mm/ rotation |
| Stroke | 20 m/ 40 m presetting |
| Grips lateral displacement | 4.2 ± 0.04 mm/ rotation |
| Idler wheel speed | 40 ± 1 rpm |
| Measurement mode | Auto/ manual presetting |
| Specimen size | Diameter 16 mm, thickness at least 6 mm |
| Emery cloth specifications | 60 # seam is less than 2 mm |
| Shift screw | 6 teeth/ inch |
| Limit rotation | 85 rotate |
| Set rotation | 84 rotation of 40 meters |
| Return form | Electric automatic reset |
| Net Weight | 75 kg |
| Dimension | 950 × 660 × 310 mm |
| Power supply | 220 V, 50 / 60Hz |
- Automatic electric lock for the rotating cylinder
- Mechanical unlocking of the cylinder for easy abrasive replacement
- Screw for adjustment of abrasion specimen
- Enables control uniformity of specific material
- Machine with metallic base plate, polished paint & zinc coating
- High quality machine design with reproducible results
- Easy to operate
DIN abrasion tester is used to determine the abrasion resistance of elastomers by the frictional loss of the rubber in products such as tires, conveyor belts, hoses, footwear, floor covering, thermoplastic amorphous polymers etc.
Rubber Testing Instruments
Mooney viscometer TMV-A10
- Control temperature range
- Normal temperature to 200°C
- Temperature display resolution
- 0.01°C
- Temperature control accuracy
- ± 0.3°
Rubber low temperature brittleness tester TRBT-A10
- Temperature range
- -60°C to 0°C
- Temperature accuracy
- ± 0.5°C
- Impact speed
- 2 m/s ± 0.2 m/s
Rubber Low Temperature Brittleness Tester TRBT-A11
- Temperature control range
- Room temperature to -70 ℃ (room temperature ≤ 25 ℃）
- Temperature accuracy
- ± 0.3 ℃
- Impact speed
- 0℃ to -30℃ around 2.5 ℃/min -30℃ to -40℃ around 2.5 ℃/min -40℃ to -70℃ around 2.0 ℃/min
No rotor rheometer TNRR-A10
- Temperature tester
- Room temperature to 200°C
- Temperature display resolution
- 0.1°C
- Temperature control accuracy
- ≤ ± 0.3°C
Paper Testing Instruments
Water absorption tester- Cobb Tester TP-C21
- Metal Cylinder inner area
- (100 ± 0.2) cm2
- Metal Cylinder height
- 50 mm
- Metal roller width
- (200 ± 0..5) mm
Automatic horizontal tensile tester TP-B12
- Sample (size) length
- 180 mm (180, 150, 100, 90, 50 mm adjustable)
- Sample width
- 15 mm
- Measuring range
- 0 to 30, 0 to 100 N,0 to 300 N, 0 to 500 N, 0 to 1000 N
Mullen burst tester TP-K11
- Measurement range
- 0 to 1600 kPa
- Accuracy
- ± 0.5 % F.S.
- Compression speed
- 95 ± 5 ml/min
Bekk Smoothness tester TP-L20
- Measuring scope
- ( 1 to 9999) s, divided in to (1 to 15) s, (15 to 300) s, (300 to 9999) s, the automatic (no. more than 200 s)
- Accuracy
- ±0.1 s within 300 s
- Vacuum system volume (ml)
- Bigger volume: 380 ± 1 Smaller volume: 38 ± 1
Plastic Testing Instruments
Charpy/ Izod Impact Tester TCI-A10
- Impact Speed & Energy (charpy)
- 2.9 m/s for 1J, 2J, 4J, 5J & 3.8 m/s for 7.5J, 15J, 25J
- Impact energy (Izod)
- 3.5 m/s for 1J, 2J, 4J, 5J, 7.5J, 15J, 25J
- Resolution of impact energy
- 0.001 J
Melt flow Indexer TMFI-A11
- Measuring range
- 0.01to 600.00 g/ 10 min (MFR), 0.01 to 600.00 cm3/ 10 min (MVR), 0.001 to 9.999 g/ cm3 (melt density)
- Measuring rate
- 0.001 S
- Temperature range
- 50 to 400°C
Falling Weight Impact Tester TFWT-A10
- Temperature range
- 10 to 35°C
- Maximum falling height
- 2000 mm
- Resolution of displacement
- 1 mm
NDT Testing Instruments
Rockwell hardness meter TRHM-A11
- Preliminary test force
- 98 N
- Total test force
- 588, 980, 1471 N
- Total test force dwell time
- 1 to 30 S
Rockwell hardness meter TRHM-A10
- Preliminary test force
- 98 N
- Total test force
- 588, 980, 1471 N
- Total test force dwell time
- 0 to 30 S
Digital low load Vickers Hardness tester TDVH-A10
- Test force
- 9.8 N, 49 N, 98 N, 196 N, 294 N, 490 N
- Hardness value symbol
- HV1, HV5, HV10, HV20, HV30, HV250
- Error range in display
- ± 3.0 %, ± 2.0 %
Digital Brinell hardness Tester TDBH-A10
- Test force
- 612.5 N, 980 N, 1225 N
- Brinell hardness test
- 1837.5 N, 2450 N, 4900 N/7350 N, 9800 N, 14700 N/29400 N
- Hardness measuring area
- 8 to 650 HBW (hard metals steel ball)
Other Testing Instruments