Vertical tensile tester TP-B20 is microprocessor controlled adopted with vertical, many pillar structure. The clamp distance can be adjusted within the specified scope. Test directly for the normal size sample and can adjust sample length and measurement range as per the needs. It is used to test the tensile strength, tensile force, tensile energy absorption, fracture length, tensile index, 180° peel strength of paper, paperboard, plastic film & other non-metal materials.
| Sample (size) length | 0 to 200 mm adjustable |
| Sample width | 15 mm |
| Measuring range | 0 to 30 N (tissue paper), 0 to 100 N,0 to 300 N, 0 to 500 N, 0 to 1000 N |
| Accuracy | ± 1 % |
| Tensile strength velocity | 1 to 399 mm/min (adjustable) |
| Tensile return velocity | 1 to 399 mm/min (adjustable) |
| Dimension (L*W*H) | 450 × 550 × 120 mm |
| Net weight | 55 kg |
| Power supply | 220 V ± 10 %, 50 Hz |
- Imported noiseless motor, with precise controls
- Large screen display with wide user interface
- Equipped with RS232 interface, connection to PC
- Easy to obtain & print the statistical results
- High automation system with messages processing & motion controls parts
- Multifunctional, flexible operation settings
- Protection against sudden power-off
Tensile horizontal tester is used in paper, paperboard, plastic film & other non-metal materials industry to test tensile strength, tensile force, tensile energy absorption, fracture & other parameters.
Paper Testing Instruments
Whiteness and chromaticity tester TP-A10
- Sample (size) length
- Diameter ≥30 mm, Thickness ≤ 40 mm
- Measurement mode
- Diffuse reflection factor Rx, Ry, Rz, stimulus value Y10, X10, Z10, chromaticity coordinates x10, y10, z10; lightness L *, chroma a * b *, chroma C * ab, hue angle h * ab, dominant wavelength λd, excitement purity Pe, color difference ΔE * ab, lightness difference ΔL *, chroma difference ΔC * ab, hue difference ΔH * ab, Hunter system L , A, b
- Stability
- ≤ 0.1 within 30 min
Automatic horizontal tensile tester TP-B11
- Sample (size) length
- 90 to 200 mm
- Sample width
- 15 mm, 25 mm, 50mm
- Measuring range
- 0 to 30, 0 to 100 N,0 to 300 N
Carton compression tester TP-I10
- Measuring range
- 0.1 to 10 kN
- Indication error
- < ± 1%
- Platen Size
- 500×500 mm (customized)
Electronic bending stiffness tester TP-E10
- Testing speed
- 200° ± 20° / min
- Test range
- 1 to 10000 mN
- Indicating Error
- ± 1 %
Plastic Testing Instruments
Melt flow Indexer TMFI-A11
- Measuring range
- 0.01to 600.00 g/ 10 min (MFR), 0.01 to 600.00 cm3/ 10 min (MVR), 0.001 to 9.999 g/ cm3 (melt density)
- Measuring rate
- 0.001 S
- Temperature range
- 50 to 400°C
Vicat softening temperature & HDT machine TVHT-A10
- Operating temperature
- Ambient temperature to 300°C
- Heating rate
- 50°C/ h (5 ± 0.5°C/ 6 min) , 120°C/ h (12 ± 1°C/ 6 min)
- Maximum temp. error with heating speed
- ± 5°C under 50°C/ h, ± 1°C under 120°C/ h
Charpy/ Izod Impact Tester TCI-A10
- Impact Speed & Energy (charpy)
- 2.9 m/s for 1J, 2J, 4J, 5J & 3.8 m/s for 7.5J, 15J, 25J
- Impact energy (Izod)
- 3.5 m/s for 1J, 2J, 4J, 5J, 7.5J, 15J, 25J
- Resolution of impact energy
- 0.001 J
Rubber Testing Instruments
DIN abrasion tester TDAT-A10
- Test arm weight
- 2.5 N
- Additional Loads
- 2.5 ± 0.1 N, 5 ± 0.1 N, 10 ± 0.1 N,
- Idler
- 150 mm
Mooney viscometer TMV-A10
- Control temperature range
- Normal temperature to 200°C
- Temperature display resolution
- 0.01°C
- Temperature control accuracy
- ± 0.3°
Rubber-weiss plasticity testing machine TRWM-A10
- Temperature range
- RT 50° to 300°
- Temperature accuracy
- ± 1°
- Measuring range
- 0.01 to 25 mm
Three roll mill machine TRMM-A10
- Mixed capacity
- 0.5 to 1 kg, 2 to 3 kg, 5 to 7 kg
- Temperature range
- RT to 300°C
- Temperature control system
- PID control
NDT Testing Instruments
Digital Brinell hardness Tester TDBH-A10
- Test force
- 612.5 N, 980 N, 1225 N
- Brinell hardness test
- 1837.5 N, 2450 N, 4900 N/7350 N, 9800 N, 14700 N/29400 N
- Hardness measuring area
- 8 to 650 HBW (hard metals steel ball)
Rockwell hardness meter (motorized type) TRHM-B10
- Preliminary test force
- 98 N
- Total test force
- 588, 980, 1471 N
- Brinell hardness test
- 306, 613, 1839 N
Digital low load Vickers Hardness tester TDVH-A10
- Test force
- 9.8 N, 49 N, 98 N, 196 N, 294 N, 490 N
- Hardness value symbol
- HV1, HV5, HV10, HV20, HV30, HV250
- Error range in display
- ± 3.0 %, ± 2.0 %
Rockwell hardness meter TRHM-A10
- Preliminary test force
- 98 N
- Total test force
- 588, 980, 1471 N
- Total test force dwell time
- 0 to 30 S